CRCA is an abbreviation of “cold rolled close anneal”. This is a steel grade in which cold rolling is done after hot rolling and pickling, to reduce the thickness of steel. Cold rolling makes the material hard
Annealing cold rolled steel involves a time and temperature controlled thermostatically process used predominantly to make steel soft again after cold reduction. Cold reduction or work hardening makes steel grain structure small and elongated. This produces high strength, but low elongation
The main advantages of annealing are in how the process improves the workability of a material, increasing toughness, reducing hardness and increasing the ductility and machinability of a metal
Standards: JIS,AISI,ASTM,GB,DIN,EN
Grade: SPCC
Width: 1250mm
Thickness: 1.0mm
ID/OD: 508/610mm
Type: in coils
Coil weight: 1.5-4tons
Technology: Cold Rolled
Surface treatment: Dull Finish, Bright Finish
Application: welded pipe/base steel for ppgi and gi/Roofing/Home Appliances
Product detail pictures:
Related Product Guide:
Being supported by an advanced and specialist IT team, we could give technical support on pre-sales & after-sales services for Quality Inspection for Hot Rolled Strip - CRC Manufacture Black Annealed Cold Rolled Steel Coil With SPCC DX51D Q195 Q235 – Ruiyi, The product will supply to all over the world, such as: Bolivia, UK, Greece, We also provide OEM service that caters to your specific needs and requirements. With a strong team of experienced engineers in hose design and development, we value every opportunity to provide best products and solutions for our customers.
By Rachel from Somalia - 2018.09.19 18:37
Speaking of this cooperation with the Chinese manufacturer, I just want to say"well dodne", we are very satisfied.
By Phyllis from Rotterdam - 2018.12.10 19:03